Polyurea Floor Coating Cost Waterproofing Floor Coating Concrete Coating

• Customization: Available
• CAS No.: 9003-11-6
• Formula: Polyether Polyol
• Model NO.: js1112
• Method: Roller
• Level: Finish Coat
• Drying Method: Air Drying
• Certification: ISO9001, ISO
• Substrate: Ceramic
• Components: Paint/Curing Agent
• Formation Mechanism: Conversion Type
• Transport Package: 20kg/Set
• Specification: 20kg/set
• Trademark: JUNESO
• Origin: Huzhou
• HS Code: 32089090
• Production Capacity: 500000kg/M

Product Description

1. Product description 

2 features

3.product application place :


4.Product test effect display

 

5. Shipping & package : customized package is accepted

Packaging Details

1. Paint is Pour into bucket and cover the bucket tight;

2. Buckets are put one by one closely with rope to bind together tightly

3. Wrapped by shrink film 3 times with pallets under;

4. Loaded by FCL/ LCL container;

6.Company profile:

7. Product Data
 

Polyaspartic Garage Floor Top Coating Data Sheet
Product Name			Polyaspartic Garage Floor Coating-                               Type A (T23090189)
Main Raw Material			Polyaspartic polyurea resin
No#	Project		Data
1	Drying time	surface dry	2H, can be walked by people
		full dry	3 days ,Also affected by local temperature
2	Tensile strength (500±50) mm/min,MPa		21.89
3	Elongation at break (500±50) mm/min,%		525
4	Tearing strength (500±50) mm/min,N/mm		78
5	Bending at low temperature		-35ºC, no cracks
6	Impermeability		0.3MPa,120min, No permeability
7	Water absorption rate %		1.9
8	Bond strength                                        (Under standard experimental conditions, MPa)		3.20 (Substrate Failure )
9	Acid treatment (2% H2SO4 solution 7d)	Tensile strength retention rate %	77
		Elongation at break %	632
		Bending at low temperature	-30ºC,no cracks
10	Alkaline treatment                 0.1% NaOH  solution +saturated Ca(OH)2 solution ,7d	Tensile strength retention rate %	78
		Elongation at break %	598
		Bending at low temperature	-30ºC,no cracks
11	Salt treatment (3%NaCI solution ,7d)	Tensile strength retention rate %	79
		Elongation at break %	603
		Bending at low temperature	-30ºC,no cracks
12	Artificial climate aging  (2745h)	Apperance	No cracks
		Tensile strength retention rate %	92
		Elongation at break %	567
		Bending at low temperature	-30ºC,no cracks
13	Water resistance                                    (indoor temperature 14d )		No cracks, no layering, no sticking, no foaming, no breakage
14	Wear resistance (750g/500r) ,mg		14
15	Impact resistance,1.0kg.m		No damage
Shanghai Juneso New Materials Co.,Ltd